WL Colmonoy 4

Home > Products > Hardfacing welding material > WL Colmonoy 4

WL Colmonoy 4

Colmonoy 4 Welding Rod - Nickel Based Alloy Hard Facing Rod High Temperature Valve Valve Sealing

Properties: Resistant to wear, heat, corrosion and abrasion

Application: Automotive, Wood&Timber, Chemical&Petrochemical, Power Generation, Oil&Gas

008615801826494

singoo@wl-allotech.com

8615801826494

WL Colmonoy 4

description1

Zipper closure 1/4 zip athletic pullovers for men. Stretchy, lightweight, fast-drying fabric for superior performance. REGULAR FIT - US standard sizes. An athletic fit that sits close to the body for a wide range of motion, designed for optimal performance and all day comfort. FEATURES - Quarter zip closure;Thumbholes on long sleeves to keep them in place during workout

Product Description

WL Allotech NiCrBSi 4 rod offers superior wear protection, retaining its hardness up to 600ºC (1000ºF) with significant resistance to oxidation, and it offers outstanding metallurgical and physical properties making them ideally suited to solving wear mechanisms such as abrasion, erosion, corrosion and high-temperatures encountered in service.

Hardness: 36-40HRC

Chemical Composition(%)

C	Si	B	Mo	Cr	W	Ni	Fe
0.4	2.4	2.1	/	10.00	/	Rest	2.8

Specification

AWS / ASME: A5.21 / SFA5.21 ERNiCr-A
Cold / Hot Abrasion	Good / Good
Erosion / Corrosion	Good / Good
Impact	Good
Magnetic	No
Deposit Layers	2 Max
Machinability	Grinding
Max. Operating Temp.	600 ºC

Packing Details

For length 350mm 500mm pack in carton each 5kg
For 1000mm packing in 5kg tube, 4 tubes in one 20kg carton
For length more than 1000mm, pack in wooden box directly

Applications

Automotive, Wood&Timber, Chemical&Petrochemical, Power Generation, Oil&Gas, Mining, Plastic&Rubber, Pulp&Paper, Dies&Molds

Type We Could Offer

Trademark	Nominal Chemical Composition										HRC	Application
Trademark	C	Cr	Si	W	Ni	Fe	Mn	Mo	Co	B	HRC	Application
WL Co1	2.45	30.0	1.0	13.0	≤3.0	≤3.0	≤1.0	≤1.0	Bal.		50-58	Valve seat insets, bearing, sawteeth, rotary ring, Pump Sleeves
WL Co3	2.4	30.5	1.0	13.0	≤3.0	≤3.0	≤1.0	≤1.0	Bal.		50-56	Valve seat insets,steel mill guide roll, wearing panel of cracker blade, etc.
WL Co4	1.0	31.0	1.0	14.0	≤3.0	≤1.0	≤0.5	≤0.5	Bal.		45-50	Hot extrusion die, dry battery industry
WL Co6	1.2	29.0	1.0	4.5	≤3.0	≤3.0	≤1.0	≤1.0	Bal.		40-46	Engine valve, high temperature valve, turbine blade
WL Co12	1.4	30.0	1.3	8.5	≤3.0	≤3.0	≤1.0	≤1.0	Bal.		44-50	Pressure valves, sawteeth screw fights
WL Co20	2.5	32.0	1.0	17.0	≤3.0	≤3.0	≤0.5	≤1.0	Bal.		54-59	Wear plate, bearing sleeve, etc.
WL Co21	0.2	27.0	1.0	0.2	≤3.0	≤2	≤1.0	≤5.5	Bal.		20-40	Fluid valve seat, turbine blades, hot forging die
WL Co25	0.05	20.0	1.0	15.0	10.0	≤2.0	≤1.5	≤1.0	Bal.		24	High temperature and corrosion-resistant valve sealing surface, pressure casting dies, etc.
WL Co31	0.5	26.0	1.0	7.5	10.0	≤3.0	≤1.0	≤1.0	Bal.		30-35	Extrusion die, steam turbine blade, etc.
WL Co32	1.8	26.0	1.2	12.0	22.0	≤1.5	≤0.5	≤1.0	Bal.		40-45	Engine inlet and exhaust valve
WL Co190	3.2	26.0	1.0	14.0	≤1.0	≤3.0	≤1.0	≤1.0	Bal.		54-60	Petroleum drill bit, mining industry
WL CoT400	0.08	8.5	2.6		1.5	≤1.5	≤1.0	28	Bal.	0.8	50-60	Valve and roller path, plastic extruder in strongly corrosive
WL CoT800	0.08	18.0	3.4		≤1.5	1.5	≤1.0	28	Bal.	0.8	52-58	Valve and roller path, plastic extruder in strongly corrosive