WL Haynes 25
WL Haynes 25
Haynes 25 L-605 cobalt based alloy used for mufflers and turbine rings
Haynes 25 (L-605) is a cobalt based alloy that combines good forming and excellent high temperature properties. The alloy is resistant to oxidation and carburization to 1900 °F. Alloy 25 can only be hardened significantly by cold working. Cold working will increase creep strength up to 1800 °F and stress rupture strength uo to 1500 °F. Strain aging at 700 - 1100 °F improve creep and stress rupture strengths below 1300 °F.
|
GB |
W-Nr. |
UNS |
France |
|
GH5605 |
2.4964 |
R30605 |
Kc20wn |
|
% |
Cr |
Co |
Ni |
W |
Si |
C |
Fe |
S |
P |
Mn |
|
Min |
19.0 |
Bal. |
9.0 |
14.0 |
|
0.05 |
|
|
|
1.0 |
|
Max |
21.0 |
11.0 |
16.0 |
1.0 |
0.15 |
3.0 |
0.03 |
0.03 |
2.0 |
|
Grade |
Density |
Melting Point |
Tensile strength,MPa |
Yield strength,MPa |
Elongation,% |
|
Haynes 25 |
9.13g/cm3 |
RT |
862 |
310 |
30 |
Outstanding high temperature strength
Oxidation resistant to 1800° F
Galling resistant
Resistant to marine environments, acids and body fluid
Jet Engine Parts: turbine blades, combustion chambers, after burner parts and turbine rings
Industrial Furnaces: mufflers and turbine rings
Medical: implantable laser-welded ballon stents for Vascular, stamped/wire EDM, or etched fabrications
Sheet, Plate, Strip AMS 5537
Billet, Rod, Bar, AMS 5759; MIL-C-24252D
Coated Electrodes AMS 5797
Bare Welding Rods & Wire AMS 5796
Forgings AMS 5759
MIL C-24252 Comp 1
_副本.jpg?x-oss-process=image/resize,w_100/quality,q_100)
.jpg?x-oss-process=image/resize,w_100/quality,q_100)
.jpg?x-oss-process=image/resize,w_100/quality,q_100)
.jpg?x-oss-process=image/resize,w_100/quality,q_100)
Contact US
Product Information
Quantity
Unit
Piece
Support order samples, customization, wholesale direct, and complete payment. If the product you look for does not have corresponding customized content, pls fill out the form below to contact us, and we will reply ASAP.