NiCr80/20 Thermal Spray Wire Nickel Alloy Wire TAFA 06C Elements Oxidation Resistance Wear Resistant Alloys

008615801826494

singoo@wl-allotech.com

8615801826494

WL NiCr8020

description1

Zipper closure 1/4 zip athletic pullovers for men. Stretchy, lightweight, fast-drying fabric for superior performance. REGULAR FIT - US standard sizes. An athletic fit that sits close to the body for a wide range of motion, designed for optimal performance and all day comfort. FEATURES - Quarter zip closure;Thumbholes on long sleeves to keep them in place during workout

Product Description

NiCr80/20 nickel-chromium system shows that chromium is quite soluble in nickel. This is a maximum at 47% at the eutectic temperature and drops off to about 30% at room temperature.Arange of commercial alloys is based on this solid solution. Such alloys have excellent resistance to high temperature oxidation and corrosion and good wear resistance.

Equivalent to: Tafa06C,PMET821,Metco8450

Surface Preparation

Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning. Recommended method of preparation is, to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.

Chemical Composition(wt%)

Nominal Composition	Cr %	Ni %
Min	20.0
Max		Bal.

Specifications

Grade	GE	PWA
NiCr80/20	B50TF119	36947

Physical Properties

Grade	Density	Melting point °C	Electrical Resistivity at 20°C Ω mm2/m
NiCr80/20	8.3g/cm3	1400	1.09

Typical Seposit Characteristics

Typical Hardness	Bond Strength	Deposit Rate	Deposit Efficiency	Machineability
HRB 90	7300 psi	11 lbs/hr/100A	65-75 %	Good

Packing Details

Diameter	DimensionTolerance	Packing	Wire Weight
2.0mm	+0/-0.05	D 270 Spool	5kg/spool
1/8"(3.17mm)	+0/-0.05	D 270 Spool	5kg/spool

Applications

Oxidation Resistance
Heating Elements
Thermocouples
High Temperature Corrosion Resistant Alloys
Wear Resistant Alloys

Type We Could Offer

Thermal spray wire-Nickel based

WL TYPE	Tafa	PMET	Metco	Size
WL-NiAl95/5	75B	885	8400	1.6/2.0/3.17mm
WL-NiAl80/20	79B	884	405	2.0/3.17mm
WL-NiCr80/20	06C	821	8450	1.6/2.0/3.17mm
WL-Monel400	70T	877	Monel	1.6/2.0/3.17mm
WL-NiCrTi	45CT	889	8500	1.6/2.0/3.17mm
WL-Inconel718	78T	818	8718	1.6/2.0/3.17mm
WL-Inconel625	71T	860	8625	1.6/2.0/3.17mm
WL-Alloy-C276	77T	876	8276	1.6/2.0/3.17mm
WL-NiCrAl(P)	73MXC	886	8443	1.6/2.0mm
WL-NiCrAlY(P)	76MXC	887	884	1.6/2.0mm
WL-NiMoAl(P)	74MXC	888	8447	1.6/2.0mm

Thermal spray wire-Iron based

WL TYPE	Tafa	PMET	Metco	Size
WL-SS420	60T	720	Metcoloy 2	1.6/2.0/3.17mm
WL-SS304/304L	80T	710	Metcoloy 1	1.6/2.0/3.17mm
WL-SS316/316L	85T	730	Metcoloy 4	1.6/2.0/3.17mm
WL-FeCrAl	Alcro	731		1.6/2.0mm
WL-FeCrBSi(P)	95MXC	273		1.6/2.0mm
WL-FeCrNiB(P)	96MXC			1.6/2.0mm
WL-Tungsten Carbide(P)	97MXC	297	Duocor	1.6/2.0mm
WL-LCr Carbide(P)	98MXC	223		1.6/2.0mm
WL-FeAl(P)	35MXC	50		1.6/2.0mm
WL-HCr Carbide(P)		226	Sm8222	1.6/2.0mm

Thermal spray wire-Copper based

WL TYPE	Tafa	PMET	Metco	Size
WL-Pure Copper				1.6/2.0/3.17mm
WL-CuSn1	05T			1.6/2.0/3.17mm
WL-CuAl8			Sprabronze AB	1.6/2.0/3.17mm
WL-CuAl10	10T	590	Sprabronze AA	1.6/2.0/3.17mm

Thermal spray wire-Zinc & Aluminium based

WL TYPE	Tafa	PMET	Metco	Size
WL-Pure Al	01T	699	Aluminum	1.6/2.0/3.17mm
WL-Pure Al Grade 1100				1.6/2.0/3.17mm
WL-Pure Zn	02Z	540	Zinc	1.6/2.0/3.17mm
WL-AlMg5			Metco AlMg	1.6/2.0/3.17mm
WL-ZnAl85/15	02A		Zn/Al	1.6/2.0/3.17mm

Thermal spray wire-Other based alloy

WL TYPE	Tafa	PMET	Metco	Size
WL-Molybdenum wire	13T	899	Sprabond	1.6/2.0/3.17mm
WL-Babbitt wire	04T	542	Sprababbitt	1.6/2.0/3.17mm
WL-Tin wire	02W	549	Metco Tin	1.6/2.0mm
WL-Ti wire	14T			1.6/2.0mm